• High Heat Resistance: Maintained structural stability at temperatures up to 140°C for 30 minutes, making it suitable for enclosures, brackets, and functional electronics components.
• 232.5% Higher Impact Strength: Delivers exceptional impact resistance (399 J/m) and high toughness, withstanding mechanical stress, drilling, and tapping without cracking or deformation.
• 88% Elongation at Break: Features outstanding flexibility and bending resistance, resisting fracture and deformation even under repeated flexing.
• PC-Like Performance & Machinability: High tensile strength (31 MPa) and 79D hardness, offering a wear-resistant, scratch-resistant finish with low shrinkage and good fluidity for effortless post-processing.
• Applications: Ideal for functional design, snap-fit assemblies, brackets, tooling, customizable parts, and weather-resistant outdoor components.
• Printing Tips for PC-Like Resin:

1. High viscosity resin — Shake the bottle thoroughly before use to ensure even consistency prior to printing.
2. Cleaning detailed models — For models with fine details, use a soft brush to clean the surface thoroughly. Ultrasonic cleaning alone may leave residue on the print.

Layer Height: 0.05 mm

Bottom Layer Count: 5-10

Bottom Exposure Time

Monochrome LCD screen: 25-45s

RGB LCD screen: 25-40s

Exposure Time

Layer Exposure Time: 3.8-4.8s

Lifting Height: 6-12 mm

Lifting Speed: 60-180 mm/min

Retracting Speed: 60-180 mm/min

Operating Conditions: Ambient Temp: 25–30°C | Humidity: <60% RH

• The settings displayed above are intended as guidance to help you find your optimal print settings. Each desktop 3D printer has its own characteristics and requires fine-tuning and optimization of these settings to achieve the best printing results.

Inslogic PC-Like Resin offers exceptional thermal stability and high mechanical performance, engineered to withstand temperatures up to 140°C for 30 minutes. As a versatile material in the Inslogic lineup, it combines 232.5% higher impact strength (399 J/m) with an impressive 88% elongation at break, providing superior fracture resistance and anti-bending performance.

Engineered for demanding engineering projects, PC-Like Resin features low shrinkage, good fluidity, and high dimensional accuracy. The printed models have a scratch-resistant and wear-resistant surface that reliably supports drilling, tapping, and mechanical post-processing. Featuring low odor and excellent weather resistance, it is the ideal choice for high-precision functional parts, enclosures, snap-fit assemblies, tooling, and durable end-use components.

Broadly compatible with 99% of DLP, SLA, and LCD 3D printers operating in the 365–405 nm range.

• Net Weight: 1 kg (35.27 oz)
• Package Dimensions: 9.25 x 5.75 x 2.64 inches
• Item Weight: 2.2 pounds
• Density (Liquid): 1.1098 g/cm³
• Solid Density: 1.1356 g/cm³
• Viscosity (25°C): 2500-3000 mPa.s
• Tensile Strength: 31 MPa
• Elongation at Break: 88%
• Flexural Strength: 46 MPa
• Flexural Modulus: 1058 MPa
• Izod Impact, Notched: 399 J/m
• Heat Deflection Temp at 0.45 MPa: 45.2 ℃
• Shore D Hardness: 79D
• *All specifications have been tested in a laboratory. Please note that material properties may vary based on part geometry, print orientation, print settings, and temperature. Certain specifications may be subject to change without prior notice.

• Technical Data Sheet (TDS) 
• Inslogic 3D Model Rose